Inconel 600 Sheet Plate Manufacturer

Incoloy 800 Plate

Steel Plate
Sizes in Stock
Alloy 800 Sheet: Thickness: 0.1 to 5.0 mm
AMS 5877 Plate:
Thickness:2.5 to 100 mm
European & American Standard: ASTM B409, ASME SB409, AMS 5877, UNS N08800, WNR 1.4876, BS 3073NA15, EN 10095, BS 3072NA15, DIN 17460, VdTüV 412 & 434, EN 10028-7
UNS N08800 Material Forms:
Plate, Sheet, Foil, Coil, Strip, Shim Sheet
cutting method
Cutting Method: Water Jet Cutting
brand
Brand:
Outokumpu, Jindal, ATI, ATI, Yakin, Special Metals, VDM, Huntington, DKC,
Origin
Origin:
USA, Korean, European, Japanese, Indian
Welding Electrodes :
INCOWELD A
Fillers :
82
ASTM A265 WNR 1.4876 Clad Plate Use :
Pressure Vessels Applications
Delivery Time:
Uganda: 17-19 Days
Panama: 25-30 Days
Syria: 7-8 Days
MTC Certificate: EN 10204 3.1 and 3.2

Supplier of nickel alloy 800 sheet in India

Incoloy 800 Plate


Stockist of ASTM B409 UNS N08800 strip and coil in Mumbai, check all specifications and offering the best prices

Incoloy 800 Plate Specification

Alloy 800 Sheet Sizes

Alloy 800 Sheet

  • Thickness: 0.1 to 5.0 mm
  • Width:0.5 to 1.0 meter
  • Length: 0.7 to 6.0 meter
Inconel 800 Plate Sizes

Inconel 800 Plate

  • Thickness: 2.5 to 100 mm
  • Width:0.05 to 2.0 meter
  • Length: 0.1 to 6.0 meter
AMS 5877 Coils Sizes

AMS 5877 Coils

  • Thickness: 0.1 to 5.0 mm
  • Width:0.5 to 1.2 meter
  • Edge: Square, Round, Rolled, Slit
Nickel Alloy 800 Strips Sizes

Nickel Alloy 800 Strips

  • Thickness:0.05 to 3mm
  • Width:5 to 200 mm
  • Packaging: Wooden Pallets, Bubble wraps etc.
Are You Looking For ?

Are You Looking For ?

  • Trade name:Ferrochronin® 800, Nickelvac® 800
  • AMS 5877
  • Processsing: Edging, Grinding, Deburring etc.
  • Welding:GMAW, GTAW, SAW, PLASMA
Global Standards

Global Standards

  • ASTM B409 | ASME SB 409
  • UNS: N08800
  • WNR: 1.4876
  • Other:BS 3073NA15, BS 3072NA15, VdTüV 412
Regarding Incoloy 800 Plate

Regarding Incoloy 800 Plate

  • Density:7.94 g/cm³
  • Melting Point:1357-1385°C | 2475-2525°F
  • Temprature Range:1500°F (816°C)
  • Life Span: 30 years
Beneficial Data

Beneficial Data

  • Hardness: Soft Hard, Quarter, and Half Hard etc.
  • Technique: Forged, Cold and Hot Rolled etc.
  • Process: Plasma, Waterjet, Laser, Oxy-propane etc.
  • Finish:Brushed, Sandblasted, Glossy, Mirror etc.
Features of Nickel alloy 800 coil

Features of Nickel Alloy 800 Coil

  • Withstand high temperature & pressure
  • Corrosion resistant
  • Excellent stress distribution
Incoloy 800 strip Applications

Incoloy 800 Strip Applications

  • Heat Treat Trays
  • Food processing
  • Furnace equipment parts
Alloy 800 Foil Marking

Alloy 800 Foil Marking

  • Material grade
  • Sizes
  • Manufacturer logo / name
  • Manufacturing date
  • ASTM/ ASME standard
Certification of sheet 1.4876

Certification of Sheet 1.4876

  • 100% Radiography Test Report
  • EN 10204/3.1B,
  • Raw Materials Certificate
  • Third Party Inspection Report
  • Certificate of Origin legalized
EN 1.4876 sheet  inspection plan

EN 1.4876 Sheet Inspection Plan

  • Non destructive test pmi test
  • Visual inspection test
  • Chemical test
  • Mechanical test
  • Destructive test
  • Third party inspection test
  • Nabl approved lab test
  • Flaring Test

 

Incoloy 800 sheet value added services

Incoloy 800 Sheet Value Added Services

  • welding
  • edge preparation
  • Bending
  • mechanical processing
  • Slitting
  • cutting to length
  • shearing
  • sawing
Alloy Incoloy 800 hot rolled plate characteristics

Alloy Incoloy 800 Hot Rolled Plate Characteristics

  • Long-lasting
  • High tensile strength
  • Durability
  • Rugged construction
  • Flexibility
BS 3072NA15 sheet documentation offered

BS 3072NA15 Sheet Documentation Offered

  • Country of Origin Certificate (Original)
  • Bill of Lading.
  • Copy of Invoice
  • Copy of Packing List indicating details of Sizes, quantity, weight, thickness etc.

Forms of Inconel Alloy 800 Plate in Stock

In Stock Incoloy 800 Sheet

Incoloy 800 Sheet

In Stock UNS N08800 Shim Sheet

UNS N08800 Shim Sheet

In Stock AMS 5877 Foil

AMS 5877 Foil

In Stock Alloy 800 Plate

Alloy 800 Plate

In Stock WNR 1.4876  Diamond Plate

WNR 1.4876 Diamond Plate

In Stock Inconel 800 Chequered Plate

Inconel 800 Chequered Plate

In Stock Nickel Alloy 800 Coil

Nickel Alloy 800 Coil

In Stock Incoloy Alloy 800 Strips

Incoloy Alloy 800 Strips

Incoloy 800 Sheet HS Code

Material HS code
Incoloy 800 sheet 72192212

 


Incoloy 800 Sheet Plate is one of the products supplied by Siddhagiri Metals and Tubes. The materials conform to International standards and specifications. ASTM B409 UNS N08800 is available in the size range of 1000 mm x 2000 mm, 1220 mm x 2440 mm, 1500 mm x 3000 mm, 2000 mm x 2000 mm, 2000 mm x 4000 mm. Our company is ISO 9001:2015 Certified and CRISIL MSE 4 Rated. We know that the dynamic needs of the sectors require products which are precise and advanced, and that is why our R&D team is fully committed to developing products and manufacturing processes which set new standards in the industry.

 

  • Form: Hot Rolled, Cold Rolled, Perforated, chequered
  • Size: 1000 mm x 2000 mm, 1220 mm x 2440 mm, 1500 mm x 3000 mm, 2000 mm x 2000 mm, 2000 mm x 4000 mm
  • Packing: Packed in Wooden Boxes, Bubble wraps, Steel Strips Bundled, or as per Customers Requests
  • Origin: Indian Origin, European Origin, Japanese Origin
  • Finish:Mirror Finish, BA Finish, 2B Finish, No. 4 Finish
  • Testing and Documents: Mill Test Certificates, EN 10204 3.1, Chemical Reports, Mechanical Reports, Destructive Test Report, Non Destructive Test Reports, PMI Test Reports, Visual Inspection Reports, Third Party Inspection Reports, NABL Approved Lab Reports

 

Properties of Incoloy 800 Alloy

Incoloy 800 Cold Forming

Cold forming of Incoloy 800 is done by procedures similar to those used for Inconel Alloy 600 and Stainless Steel. The work-hardening rate for Inconel 800, is higher than the rate for mild steel but lower than that for Type 304 stainless steel. The work-hardening rate for Incoloy 800 is essentially the same as the rate for Inconel 600.

Incoloy 800 Hot Forming

Hot forming of Incoloy 800 is done in the temperature range of 1600 to 2200°F (870 to 1200°C). Heavy forging should be done at temperatures from 1850°F to 2200°F (1010°C to 1200°C). Forming at temperatures between 1200 and 1600°F (650-870°C) can result in cracking of the workpiece.

 

The rate of cooling following hot forming is not critical with respect to thermal cracking. However, the alloy is subject to carbide precipitation in the 1000-1400°F (540- 760°C) temperature range and should be cooled rapidly through that range to avoid sensitization.

Incoloy 800 Machining

Incoloy 800 is readily machined by standard methods. Turning operations can be performed with high metal removal rates, good tool life, and good surface finish using coated carbide tools. Good results have also been obtained with high-speed-steel tools, which are better for interrupted cutting.

Coated carbide tools have shown good life at cutting speeds of 110-190 sfpm (33.5-57.9 m/min) and a feed of 0.008-0.035 ipr (0.20-0.89 mm/rev.). High speed steel tools have been shown to have good life at cutting speeds of 35- 95 sfpm (10.7-29.0 m/min) and a feed of 0.008-0.035 ipr (0.20-0.89 mm/rev.).

 

Incoloy 800 Welding

Incoloy 800 has good weldability by all welding processes. Material to be welded must be thoroughly clean, and the proper joint designs must be used. For shielded metal-arc welding of Alloy 800, the recommended welding product is Inco-Weld a Electrode. For gas-tungsten-arc, gas-metal-arc, and submerged-arc welding, Inconel Filler Metal 82 is recommended. Incoflux 4 Submerged Arc Flux is used with the submerged-arc process. These products may be used for most dis-similiar welding requirements with Incoloy 800 as well.

 

Incoloy 800 Heat Treatment

All material to be heated must be clean. Oil, paint, grease, shop soil and other foreign substances must be removed prior to the heating operation. Heating must be performed in a low-sulfur atmosphere. Open heating must be done with low-sulfur fuel, and the furnace atmosphere must be maintained in a reducing condition to prevent excessive oxidation. Because of the readiness with which chromium is oxidized into a refractory oxide by air, carbon dioxide or water vapor, alloy 800 cannot be bright annealed in the usual industrial annealing furnace. Under closely controlled conditions, the alloy can be bright annealed in dry, pure hydrogen (dew point of -73°F (-58°C) or lower, less than 0.004% by volume water, and less than 0.007% by volume air).


Exporter of AMS 5877 sheets, available stock in thicknesses between 0.1 and 5.0 mm and widths between 0.5 and 1.0 metres for use in heat exchangers

Incoloy 800 plate

Supplier of Werkstoff NR. 1.4876 foils and shim sheets, in custom sizes to meet specific requirements

Incoloy 800 Alloy Sheet Plate Sizes in Stock

Material Size Thickness Specification Make
Incoloy 800 Plate / Sheet / Flat / Coil 1250 mm x 2500 mm 0.1mm to 12 mm Thk IS, BS, ASTM, UNS Indian, European and Japanese origin
1000 mm x 2000 mm
1220 mm x 2440 mm (4' x 8')
1500 mm x 3000 mm
2000 mm x 2000 mm
2000 mm x 4000 mm

Inconel 800 Plate Properties

  • Chemical Properties
  • Mechanical Properties
  • Physical Properties
  • C Ti Mn Fe S Si Cr Ni Cu Al
    MIN - 0.150 - 39.500 - 19.000 30.000 - 0.150
    MAX 0.100 0.600 1.500 0.015 1.000 23.000 35.000 0.750 0.600
  • Yield Str0.2% Proof(MPa) Tensile Str(MPa) Elong(% in 2mm) Hardness HV
    205 520 30.00 -
    - - - 182
  • Density lb/in³ 0.287
    g/cm³ 7.94
    Specific Heat (32-212°F), Btu/lb•°F 0.11
    (0-100°C), J/kg•°C 460
    Melting Range °F 2475-2525
    °C 1357-1385
    Curie Temperature °F -175
    °C -115
    Permeability 70°F (21°C) & 200 oersted (15.9 kA/m)  
    Annealed 1.014
      Hot-Rolled 1.009

Find Inconel 800 hot-rolled and cold-rolled plate in unusual sizes, order now!

Additional service : Small quantity | Custom order | hard to find items | Sourcing from other countries