Hastelloy C22 Round Bar Manufacturer

Hastelloy C22 Round Bar

Round Bar
Sizes in Stock
WNR 2.4602 Round Bar: Dia:  3 - 600 mm, Length: 0.5 - 6.0 meter
Hex Bar
Alloy C22 Hex Bar: Dia:  3 - 180 mm
Flat Bar
Nicrofer® 5621 Flat Bar: Thickness: 0.5 - 200 mm, Width: 1.5 - 250 mm
Square Bar
UNS N06022 Square Bar:Side Width: 2 - 200 mm
European & American Standard: ASTM B574, ASME SB574, UNS N06022, DIN 17752, ISO 9724, ISO 9723, DIN 17753
condition
Condition: Annealed, PH, H&T, Cold-worked, Hot worked
edges
Edges: Square, Round, Slit, and V Edge
brand
Brand: Yakin, Outokumpu, ATI, Mukund, AventBar, Ratnaveer, Gloria, triton bar
tolerance
Tolerances: H11, H10, K10, H9, H12, K11, K9, H8, K12, H13
Delivery Time:
Malaysia : 6-8 Days
Canada : 25-30 Days
MTC Certificate: EN 10204 3.1 and 3.2

Supplier of Nickel Alloy C22 rod in India at a fair price

Hastelloy C22 Round Bar


Buy WNR 2.4602 hex bar diameter from 3 - 180 mm with black and bright surface finish

Hastelloy C22 Round Bar Specification

Nickel Alloy C22 Round Bar Sizes

Nickel Alloy C22 Round Bar

  • Diameter: 3 - 600 mm
  • Length: 0.5 - 6.0 meter
  • Surface:Black, Bright, Polished, Pickled
Haynes Alloy C22 Hex bar Sizes

Haynes Alloy C22 Hex bar

  • Inscribed Diameter: 3 - 180 mm
  • Length:0.5 - 6.0 meter
  • Supply State: Annealed, Hardened, Turned & rough etc.

Stockist of Alloy C22 flat bar with stock ranging from 0.5 to 200 mm in thickness and 1.5 to 250 mm in width in Mumbai

Alloy C22 Square bar Sizes

Alloy C22 Square bar

  • Side width: 2 - 200 mm
  • Length: 0.5 - 6.0 meter
  • Packaging: Plastic Bag, Wooden Case
WNR 2.4602 Flat bar Sizes

WNR 2.4602 Flat bar

  • Thickness: 0.5 - 200 mm
  • Width: 1.5 - 250 mm
  • Length: 0.5- 6.0 meter
Are You Searching?

Are You Searching?

  • Trade name: Hastelloy C22®, Nicrofer® 5621
  • Form: Square, Round, Rectangular, Hex
  • Condition: Annealed, PH, H&T, Cold, Hot worked
  • Origin: Janpanese, American, European, Russia etc.
Worldwide Standards

Worldwide Standards

  • ASTM B574 | ASME SB 574
  • UNS: N06022
  • WNR: 2.4602
  • Other: DIN 17752, ISO 9724, ISO 9723, DIN 17753
Ready stock of Haynes Alloy C22 square and rectangular bar with temprature range 1121°C - 2050°F
About Hastelloy C22 Round Bar

About Hastelloy C22 Round Bar

  • Melting Point:1399°C (2550°F)
  • Density: 75°F
  • Temprature Range: 1121°C - 2050°F
  • Life Span: 25-30 years
Advantageous Information

Advantageous Information

  • Tolerance:H8 to H13 or K9 to K12
  • Technique: Cold and Hot Rolled, Forged etc.
  • Shape: Hexagon, Round, Square, Rectangular etc.
  • Testing:Destructive And Non Destructive Test
 Werkstoff NR. 2.4602 bar surface

Werkstoff NR. 2.4602 bar surface

  • Hairline
  • Bright
  • Hot rolled pickled
  • Cold drawn

 

Alloy Hastelloy C22 Bar value added services

Alloy Hastelloy C22 Bar value added services

  • Trepanning, grinding, PSQ, and turned
  • ground & polished bar
  • Turnkey inventory stocking programs
  • Same day custom cutting capability
 Haynes Alloy C22 bright drawn round bar brand

Haynes alloy C22 bright drawn round bar brand

  • Yakin, Outokumpu,
  • Mukund, AventBar
  • Ratnaveer, ATI,
  • Gloria, triton
Certifications of Hastelloy 2.4602 hexagonal bar

Certifications of Hastelloy 2.4602 hexagonal bar

  • Heat treatment charts
  • Third party inspection report
  • DFARS compliant
  • HS code commercial invoice
  Hastelloy C22 annealed bar features

Hastelloy C22 annealed bar features

  • Stress Rupture and Creep Resistance
  • Oxidation Resistance
  • Weldability and Formability
  • Exceptional Corrosion Resistance
 DIN 2.4602 precision bar benefits

DIN 2.4602 precision bar benefits

  • Reduced Maintenance
  • Versatility
  • Increased Equipment Lifespan
  • Improved Efficiency
 Hastelloy alloy C22 forged cold drawn bar applications

Hastelloy alloy C22 forged cold drawn bar applications

  • Pollution Control Industry
  • Nuclear Industry
  • Oil and Gas Industry
  • Chemical Processing Industry
Alloy C22 peeled round bars markings

Alloy C22 peeled round bars markings

  • Manufacturer’s name or custom logo – on request
  • Method of manufacturing
  • Nominal size
  • Material grade


Get complete information about durable and robust Haynes Alloy C22 bright bars and shafts. Check Hastelloy C22 bar properties
Hastelloy C22 Round Bar


Hastelloy C22 Round Bar fabricated with high quality raw materials is exported and supplied by Siddhagiri metals and Tubes. We are one of the trusted suppliers of ASTM B574 UNS N06022 Bars. We offer products at highly competitive prices and deliver consignment within stipulated time. Our Pipe inventory is available in random lengths or cut to specific lengths to meet your exact requirements. Our materials are approved by Saudi ARAMCO.


Round bars are most frequently used to make parts such as gears, shafts, axles, and flywheels for rotating machinery applications. Round Bars can also be engineered and used for manufacturing of seamless pipe and tubing used in oil drilling, military, and other applications. Hastelloy Round bars conform to ASTM, UNS, ASME, UNS, ANSI, EN standards and specifications. Round Bar is available in a wide variety of sizes ranging from 10 mm to 125 mm. Hastelloy Bar available in following forms Round Bar, Hex Bars, Flat Bar, Square Bar. Round bars are typically used in Engineering Construction, Residential Construction, Non-Residential Construction, Mining Infrastructure, Transport and Storage Manufacturing.


Siddhagiri Metals and Tubes offers a comprehensive range of Hastelloy Bar which is available in Alloy and Stainless Steel grades. We pride ourselves on supplying Round Bar products to suit your exact requirements. Our Round bars are finished according to, En, BS, ANSI, ASME specifications. The length of the round bar is 50 mm to 6000 mm long and it can be Single Random, Double Random and Cut Length. The characteristics of high resistance to thermal oxidation, corrosion resistance and high strength in our round bar meet the requirements for use in numerous applications within the aerospace, chemical processing, thermal processing, oil & gas, pharmaceutical and bio synthetic and motorsport industries. We supply ASTM B574 round bars with diameters between 0.5 mm to 500 mm.


Our company has been exporting Hastelloy C22 Round bars Globally and has attained a recognition in many countries. We have exported to countries like Europe, Australia, Japan, Indonesia, South Africa, Thailand, UAE, Qatar, etc.


  • Origin: Japanese Origin ,Indian Origin, European Origin.
  • Testing and Documents: Non Destructive Test Reports, Mill Test Certificates, Chemical Reports, Mechanical Reports,EN 10204 3.1, Destructive Test Report, PMI Test Reports, Visual Inspection Reports, NABL Approved Lab Reports ,Third Party Inspection Reports,
  • Packing: Bubble wraps, Packed in Wooden Boxes, Steel Strips Bundled, or as per Customers Requests

Hastelloy C22® Round Bar Sizes in Stock

Material Diameter Length Make
Hastelloy C22 Round Bar, Hastelloy C22 Flat Bar, Hastelloy C22 Hex Bar 0.5 mm to 500 mm 50 mm to 6000 mm Long Indian, European and Japanese origin

Forms of Hastelloy C22 Bar in Stock.

In Stock Hastelloy C22 square bar Supplier

Hastelloy C22 square bar

In Stock Nickel alloy C22  hex bar supplier

Nickel alloy C22 hex bar

In Stock Hastelloy 2.4602  flat bar supplier

Hastelloy 2.4602 flat bar

In Stock Nickel C22 bright bar

Nickel C22 bright bar

In Stock  DIN 2.4602   round bar

DIN 2.4602 round bar

In Stock Hastelloy alloy C22  rectangle bar

Hastelloy alloy C22 rectangle bar

In Stock ASTM B574 UNS N06022  forged bar

ASTM B574 UNS N06022 forged bar

In Stock  UNS 6022   polished bar

UNS 6022 polished bar


In Stock Nicrofer® 5621 cold drawn bar

Nicrofer® 5621 cold drawn bar



HS Code of Nickel Alloy C22 Round Bar

Product Description HS Code
Hastelloy C22 round bar 75051220
 

WNR 2.4602 Flat bar Chemical Composition

  • Chemical Properties
  • Mechanical Properties
  • Physical Properties
  • C W Mn Fe S Si Cr Ni Co Mo P V
    MIN - 2.500 - 2.000 - - 20.000 Bal - 12.500 - -
    MAX 0.015 3.500 0.500 6.000 0.020 0.080 22.500 2.500 14.500 0.020 0.350
  • Yield Strength
    0.2% Proof
    (MPa)
    Tensile strength
    (MPa)
    Elongation
    (% in 50mm)
    Hardness
    (HRB)
    MIN 310 690 45.00  
    MAX       100
  • Density lb/in³ 0.311
    g/cm³ 8.61
    Specific Heat Btu/lb•°F 0.091
    J/kg•°C 381
    Melting Range °F 2464-2529
    °C 1351-1387
    Permeability 200 oersted (15.9 kA/m) ≤1.001
    Young's Modulus 103 ksi 30.3
    GPa 209
    Electrical Resistivity ohm•circ mil/ft 730.7
    microhm•m 1.215
    Coefficient of Expansion 70-200°F,106 in/in•°F 6.9
    21-193°C, μm/m•°C 12.42

Additional service : Small quantity | Custom order | hard to find items | Sourcing from other countries


Properties of Hastelloy C22 alloy

Hastelloy C22 Cold Forming

Cold forming of Hastelloy C22 is performed by standard methods as high-nickel alloys. The work-hardening rate of the alloy is done through cold hardening process. Hastelloy C22 is some-what softer in the annealed condition and requires lower forces for deformation.The Alloy is treated with cold picking liquid solutions.There is the formation of the oxide film on the Hastelloy C22 product form. The cold forming process of the Hastelloy is done by bathing the element in caustic solution with the molten state.The process is further followed by acid pickling at extremely high temperature. The descaling process is one of the cold forming process involving three steps:

  • —The Descaling salt bath process.
  • —The Sodium hydride reducing salt bath process.
  • —The DGS oxidising salt bath process.

Hastelloy C22 Hot Forming

Alloys can be hot worked into multiple shapes and forms.The hot forming should be done in a temperature within 1600°F and 2250°F (870°C-1230°C). Their resistance to deformation increases because of the less temperature in hot working range. Hot working temperatures for Hastelloy C22 are very high so a necessary precaution must be taken while performing the hot forming process. After annealing is done it should be quickly followed by cold quenching which will help the metal to retain its property.

Hastelloy C22 Machining

Hastelloy C22 is classified as moderate to difficult when machining, however these alloys can be machined using conventional production methods at satisfactory rates. During the machining processes these alloys work harden rapidly, generate high heat during cutting, weld to the cutting tool surface and offer high resistance to metal removal because of their high shear strengths.

Hastelloy C22 Welding

Hastelloy C22 is known to have good weldability. The most common welding processes used to weld the Hastelloy C22 are the gas tungsten arc welding (GTAW / “TIG”), gas metal arc welding (GMAW / “MIG”), and shielded metal arc welding (SMAW / “Stick”) processes. In addition to these common arc welding processes, other welding processes such plasma arc welding (PAW), resistance spot welding (RSW), laser beam welding (LBW), and electron beam welding (EBW) are used. Submerged arc welding (SAW) is generally discouraged as this process is characterized by high heat input to the base metal, which promotes distortion, hot cracking, and precipitation of secondary phases that can be detrimental to material properties and performance.

Hastelloy C22 Heat Treatment

Heat treatment is done in various procedures which involve various process. Firstly after solution annealing treatment followed by quenching to lock in the high-temperature structure. After that cooled metal is used for the further working process.