Round Bar Manufacturer

316ti Stainless Steel Round Bar

Round Bar
Sizes in Stock
SS 316ti Round Bar: Dia:  4 to 500mm, Length: 1- 6.0 meter
Hex Bar
ASTM A276 Type 316Ti Hex Bar: Dia:  18 -57mm
Flat Bar
UNS S31635 Flat Bar: Thickness: 2-150 mm, Width: 1- 6.0 meter
Square Bar
WNR 1.4571 Square Bar:Side Width: 18 - 47mm
European & American Standard: ASTM A276, ASME SA 276, ASTM A479, ASME SA 276, UNS S31635, WNR 1.4571, BS 320S31, AFNOR Z6CNDT17‐12
condition
Condition:T, A, B, H, S Condition
edges
Edges: Round, Slit, V, Square Edge
brand
Brand: Mukund, Outokumpu, ATI, AventBar, Ratnaveer, Triton, Yakin, Gloria
tolerance
Tolerances: K10, H11, K9, H12, H10, H8, K11, K12, H13, H9
Delivery Time:
Kazakhstan : 6-8 Days
Saudi Arabia : 7-8 Days
MTC Certificate: EN 10204 3.1 and 3.2

ASTM A276 Type 316Ti Rod Manufacturer in India With MTC

316ti Stainless Steel Round Bar


SS 316Ti Flat bar With Width Ranging From 12.7 to 254 mm in Mumbai At Factory Price

316ti Stainless Steel Round Bar Specification

UNS S31635 Round Bar Sizes

UNS S31635 Round Bar

  • Length: 1- 6.0 meter
  • Diameter: 4 to 500mm
  • Finish: Polished, Rough Turned, NO.4
SS 316TI Flat bar Sizes

SS 316TI Flat bar

  • Width:12.7 to 254 mm
  • Thickness: 2-150 mm
  • Length: 1- 6.0 meter

Large Selection of UNS S31635 Hex and Square Bar in various supply state like H&T, PH, ANN etc. with Custom Packaging

WNR 1.4571 Square bar Sizes

WNR 1.4571 Square bar

  • Length:1- 6.0 meter
  • Size: 18 - 47mm
  • Packaging: Bubble Wraps, Wooden Box, Bundled
ASTM A276 Type 316Ti Hex bar Sizes

ASTM A276 Type 316Ti Hex bar

  • Length:1- 6.0 meter
  • Size:18 -57mm
  • Supply State: PH, H&T, ANN
Cut to Size WNR 1.4571 Bright and rectangular bar in European and American Origin with Various conditions
Are You Searching?

Are You Searching?

  • Condition: Condition S, H, A, B, T
  • Trade name:Polarit 761, Supra316Ti, Nirosta 4571
  • Origin: Russia, European, American, Janpanese, etc.
Worldwide Standards

Worldwide Standards

  • ASTM A276 | ASTM A479
  • UNS: S31635 | WNR:1.4571
  • Other: BS 320S31, AFNOR Z6CNDT17‐12
316TI Stainless Steel Round Bar Melting Point

316TI Stainless Steel Round Bar Melting Point

  • Density:7.99 g/cm3
  • Melting Point:1400 °C
  • Temprature Range:1149-1260°C
  • Shape:Square, Hex, Round, Rectangle
ASTM A276 Type 316Ti  Bar Testing

ASTM A276 Type 316Ti Bar Testing

  • Technique: Forged, Rolled
  • Testing: Destructive and Non Destructive
  • Service: Cutting, Shearing, Heat Treatment
  • Tolerance: H8 to H13, K9 to K12

 

 INOX 316Ti Rod Value Added Service

INOX 316Ti Rod Value Added Service

  • Chemical Milling
  • Heat Treatment
  • Surface Machining
  • Production Bar Cutting
  • Custom Packing
  • Folding
  • Rigidizing

 

 

 ASTM A276 grade 316Ti Bar Weight Formula

ASTM A276 Grade 316Ti Bar Weight Formula

  • A276 Gr 316Ti hex bar: Size (mm) X Size (mm) X 0.00680 = Wt. per Mtr.
  • SUS 316Ti round bar: Diameter (mm) X Diameter (mm) X 0.00623 = Wt. per Mtr.
  • SS 316Ti flat bar: Width (mm) X Thickness (mm) X 0.00798 = Weight per Mtr.
  • A276 tp316Ti square bar: Size (mm) X Size (mm) X 0.00788 = Wt. per Mtr.
Origin of A276 type 316Ti forged bar

Origin of A276 type 316Ti forged bar

  • European, Indian
  • Russia, Korean
  • USA
 A276 tp316Ti Annealed Bar Features

A276 tp316Ti Annealed Bar Features

  • Excellent formability
  • High-temperature
  • Ductility
 Werkstoff Nr. 1.4571 Bar Shape

Werkstoff Nr. 1.4571 Bar Shape

  • Hexagonal
  • Hollow
  • Square
  • Rectangular
  • Round

 

 SS 1.4571 rounds  Tolerances

SS 1.4571 Rounds Tolerances

  • H10
  • H12
  • K12 or custom
  • H9
  • H13
  • K10
  A276 tp316Ti square bar Life Span

A276 tp316Ti Square Bar Life Span

  • Over 50 years

   ASTM A276 grade 316Ti rectangular bar Life Span

ASTM A276 grade 316Ti rectangular bar elongation

  • 35% Min
SUS 316Ti bloom   Payment term

SUS 316Ti bloom Payment term

  • Paypal
  • TT
  • LC
 INOX 316Ti hex bar  Payment term

INOX 316Ti hex bar delivery time

  • 15-20 days if its not in stock
  • Generally it is 7-10 days if its in stock


A276 tp316Ti Stock In Custom Shape and Value Added Services Like Shearing, Cutting and Heat Treatment, Refer Properties

Forms of AISI 316Ti Stainless Steel Bars in Stock.

In Stock 316Ti Stainless Steel Square Bar Supplier

316Ti Stainless Steel Square Bar

In Stock Stainless Steel 316Ti  Hex Bar Supplier

Stainless Steel 316Ti Hex Bar

In Stock SS 316Ti  Flat Bar Supplier

SS 316Ti Flat Bar

In Stock AISI 316Ti Round   Bar Supplier

AISI 316Ti Round Bar


In Stock 1.4571 AISI 316Ti Cold Rolled Rectangle  Bar Supplier

1.4571 Cold Rolled Rectangle Bar


In Stock AISI 316Ti Stainless Steel  Bright  Bar Supplier

INOX 316Ti Stainless Steel Bright Bar



In Stock SUS 316Ti Stainless Steel  Polished  Bar Supplier

SUS 316Ti Stainless Steel Polished Bar

In Stock ASTM A276 UNS S31635  Cold Drawn  Bar Supplier

ASTM A276 UNS S31635 Cold Drawn Bar

In Stock ASTM A276 Type 316Ti  Forged Bar Supplier

ASTM A276 Type 316Ti Forged Bar


Siddhagiri Metals and Tubes offers a comprehensive range of Stainless Steel Round Bar which is available in Alloy and Stainless Steel grades. We pride ourselves on supplying Stainless Steel Bars to suit your exact requirements. Our Round bars are finished according to En, BS, ANSI, ASME specifications like ASTM A479 UNS S31635 and ASTM A276 UNS S31635. The length of the round bar is 50 mm to 6000 mm long and it can be Single Random, Double Random and Cut Length.

 

The characteristics of high resistance to thermal oxidation, corrosion resistance and high strength in our round bar meet the requirements for use in numerous applications within the aerospace, chemical processing, thermal processing, oil & gas, pharmaceutical and bio synthetic and motorsport industries. We supply SS 316Ti round bars with diameters between 0.5 mm to 500 mm. Our company has been exporting SS 316Ti Bars Globally and has attained a recognition in many countries. We have exported to countries like Europe, Australia, Japan, Indonesia, South Africa, Thailand, UAE, Qatar, etc.


HS Code of 316ti Stainless Steel Round Bar

Product Description HS Code
316ti Stainless Steel round bar 72221119
 

SS 316ti Round Bar Properties

  • Chemical Properties
  • Mechanical Properties
  • Physical Properties
  • C Ni Mn P S Si Cr Mo
    MIN 0.040 10.000 - - - - 16.000 2.000
    MAX 0.100 14.000 2.000 0.040 0.030 1.000 18.000 3.000
  • Yield Strength
    0.2% Proof
    (MPa)
    Tensile strength
    (MPa)
    Elongation
    (% in 50mm)
    Hardness
    (HRB)
    MIN 170 485 40.00  
    MAX       95
  • Density kg/dm³ 8
    Modulus of elasticity GPa 200
    Thermal conductivity W/m°C 15
    Heat capacity J/kg°C 500
    Electrical resistivity µΩm 0.75
    Poissons ratio   0.3


Additional service : Small quantity | Custom order | hard to find items | Sourcing from other countries

Properties of AISI 316Ti Stainless Steel

316Ti SS Cold Forming

316Ti is readily brake or roll formed into a variety of parts. It is also suited to stamping, heading and drawing but post work annealing is recommended to relieve internal stresses. Cold working will increase both strength and hardness of 316Ti stainless steel.

316Ti SS Hot Forming

All common hot working processes can be performed on 316Ti stainless steel. Hot working should be avoided below 927°C. The ideal temperature range for hot working is 1149-1260°C. Post-work annealing is recommended to ensure optimum corrosion resistance.

316Ti SS Machining

316Ti stainless steel has good machinability. Machining can be enhanced using the following rules: Cutting edges must be kept sharp. Dull edges cause excess work hardening. Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material. Chip breakers should be employed to assist in ensuring swarf remains clear of the work. Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.

316Ti SS Welding

Fusion welding performance for 316Ti stainless steel is excellent both with and without fillers. Grade 316Ti may be used as an alternative to 316 in heavy section welds. Oxyacetylene welding has not been found to be successful for joining of 316 stainless steel.

316Ti SS Heat Treatment

316Ti stainless steel cannot be hardened by heat treatment. Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.